Dual Wall Flame Adhesive Lined Clear Heat Shrink Tubing
DWRS-125G is a cross-linked polyolefin tube that is extruded with an inner layer of adhesive. The inner layer of adhesive, with superior sealing capability, is also a buffer against mechanical strain. Dual wall heat shrink tubing is designed to provide superior sealing against water, corrosive gas, and chemicals.
Structure
Technical Performance
Property | Typical data | Test method/condition |
Tensile strength | ≥12MPa | ASTM D 2671 |
Elongation at break | ≥400% | ASTM D 2671 |
Tensile strength after heat aging | ≥11MPa | 158℃ ×168h |
Elongation after heat aging | ≥350% | 158℃ ×168h |
Longitudinal change | 0~+10% | ASTM D 2671 |
Flammability | Self extinguishing in 30 sec. | AMS-DTL-23053/4 |
Dielectric strength | ≥15kV/mm | IEC 60243 |
Volume resistivity | ≥1014Ω.cm | IEC 60093 |
Technical Performance of Adhesive
Technical Performance of Adhesive
Property | Typical data | Test method/condition |
Softening point | 95±5°C | ASTM E 28 |
Water absorption | <0.5% | ASTM D 570 |
Peel strength(PE) | ≥120N/25mm | ASTM D 1000 |
Peel strength(AI) | ≥80N/25mm | ASTM D 1000 |
Technical Performance of Adhesive
Dimension
Size(mm) | As supplied D(mm) | After full recovery (mm) | Standard Package |
Inner diameter d | Wall thickness w1 | Thickness of adhesive layer w2 | (M/Roll or M/PCS) |
Φ3.2 | ≥3.0 | ≤1.00 | ≥1.00 | 0.50 | 200 |
Φ4.8 | ≥4.8 | ≤1.50 | ≥1.00 | 0.50 | 100 |
Φ6.4 | ≥6.0 | ≤2.00 | ≥1.00 | 0.50 | 100 |
Φ7.9 | ≥7.9 | ≤2.70 | ≥1.30 | 0.50 | 100 |
Φ9.5 | ≥9.0 | ≤3.00 | ≥1.40 | 0.60 | 50 |
Φ12.7 | ≥12.0 | ≤4.00 | ≥1.60 | 0.80 | 25 |
Φ15.0 | ≥15.0 | ≤5.00 | ≥1.80 | 0.80 | 25 |
Φ19.1 | ≥19.0 | ≤6.00 | ≥2.10 | 0.80 | 25 |
Φ25.4 | ≥25.4 | ≤8.00 | ≥2.40 | 1.00 | 25 |
Φ30.0 | ≥30.0 | ≤10.0 | ≥2.40 | 1.00 | 25 |
Φ39.0 | ≥39.0 | ≤13.0 | ≥2.40 | 1.00 | 1.2 |
Φ50.0 | ≥50.0 | ≤19.0 | ≥2.40 | 1.00 | 1.2 |
Size(mm) | As supplied D(mm) | After full recovery (mm) | Standard Package |
Inner diameter d | Wall thickness w1 | Thickness of adhesive layer w2 | (M/Roll or M/PCS) |
Φ4.0 | ≥4.0 | ≤1.00 | ≥1.00 | 0.50 | 200 |
Φ6.0 | ≥6.0 | ≤1.50 | ≥1.00 | 0.50 | 100 |
Φ8.0 | ≥8.0 | ≤2.00 | ≥1.00 | 0.50 | 50 |
Φ12.0 | ≥12.0 | ≤3.00 | ≥1.40 | 0.60 | 25 |
Φ16.0 | ≥16.0 | ≤4.00 | ≥1.60 | 0.80 | 25 |
Φ18.0 | ≥18.0 | ≤4.50 | ≥1.60 | 0.80 | 25 |
Φ20.0 | ≥19.0 | ≤5.00 | ≥1.80 | 0.80 | 25 |
Φ24.0 | ≥24.0 | ≤6.00 | ≥2.10 | 0.80 | 25 |
Φ32.0 | ≥32.0 | ≤8.00 | ≥2.40 | 1.00 | 1.22 |
Φ40.0 | ≥40.0 | ≤10.0 | ≥2.40 | 1.00 | 1.22 |
Φ52.0 | ≥52.0 | ≤13.0 | ≥2.40 | 1.00 | 1.22 |
Technical Performance of Adhesive
Чаро моро интихоб кунед:
1. Шумо метавонед маводи комилро мувофиқи талаботи худ бо нархи ҳадди ақалл дастрас кунед.
2. Мо инчунин Reworks, FOB, CFR, CIF ва нархҳои интиқоли хонаро пешниҳод менамоем. Мо ба шумо пешниҳод менамоем, ки барои интиқол, ки хеле сарфакор хоҳад буд, созед.
3. Маводҳое, ки мо пешниҳод мекунем, аз шаҳодатномаи санҷиши ашёи хом то изҳороти ниҳоии андозагирӣ комилан тафтишшаванда мебошанд. (Ҳисоботҳо мувофиқи талабот нишон дода мешаванд)
4. Кафолати электронӣ барои посух додан дар давоми 24 соат (одатан дар ҳамон соат)
5. Шумо метавонед алтернативаҳои саҳҳомӣ, таҳвили осиёбро бо кам кардани вақти истеҳсолӣ ба даст оред.
6. Мо пурра ба мизоҷони худ бахшидаем. Агар пас аз баррасии ҳама вариантҳо қонеъ кардани талаботи шумо имкон надиҳад, мо шуморо бо ваъдаҳои бардурӯғ, ки муносибатҳои хуби муштариёнро эҷод мекунанд, гумроҳ намекунем.
Сафари завод
БО МО ТАМОС ГИРЕД
Масъули Тамос:Хонум Ҷессика Ву
Почтаи электронӣ :sales@heatshrinkmarket.com
WhatsApp/Wechat : 0086 -15850032094
АДРЕС:№88 Роҳи Хуайюан, Парки саноатии Аоксин, шаҳри Муду, ноҳияи Вузҳон, Сучжоу, Чин